Properties |
Unit |
Value |
Test Method |
MFI (190°C/2.16KG) |
gr/10 min |
1.7-2.3 |
ASTM D-1238 |
DENSITY |
gr/ml |
0.918-0.922 |
TSTM 209 B |
SOFTENING POINT |
°C |
92-96 |
ASTM D-1525 |
HAZE |
% |
15 MAX |
ASTM D-1003 |
GLOSS @ 60°C |
gu |
60 min |
ASTM D-523 |
Elongation @Break (MD) |
% |
330 min |
ASTM D-882 |
Elongation @Break (TD) |
% |
600 min |
ASTM D-882 |
tensile @Break (MD) |
kg/cm2 |
160 min |
ASTM D-882 |
dart impact |
gr |
100 min |
ASTM D-1709 |
Properties |
Unit |
Value |
Test Method |
MFI (190°C/2.16KG) |
gr/10 min |
0.68-0.85 |
ASTM D-1238 |
DENSITY |
gr/ml |
0.917-0.922 |
TSTM 209 B |
Vicat SOFTENING Temp |
°C |
93-97 |
ASTM D-1525 |
Elongation @Break(MD) |
% |
300 min |
ASTM D-882 |
Elongation @Break(TD) |
% |
450 min |
ASTM D-882 |
tensile @Break (MD) |
kg/cm2 |
170 min |
ASTM D-882 |
HDT |
°C |
30-36 |
ASTM D-648 |
Dart Impact |
gr |
120 min |
ASTM D-1709 |